Show simple item record

dc.contributor.advisorPatricio Vildosolaes
dc.contributor.authorDel Real, María de los Ángeles
dc.contributor.editorFacultad de Odontologíaes
dc.date.accessioned2015-10-19T19:36:33Z
dc.date.accessioned2016-08-02T20:47:18Z
dc.date.available2015-10-19T19:36:33Z
dc.date.available2016-08-02T20:47:18Z
dc.date.issued2015-10-19
dc.identifier.urihttp://repositorio.unab.cl/xmlui/handle/ria/1882
dc.description.abstractRESUMEN El fracaso más común en la rehabilitación de una pieza tratada endodónticamente mediante poste de fibra es su decementación. Actualmente la adhesión intraradicular es uno de los temas con mayor controversia debido a los múltiples sistemas existentes en el mercado, dentro de los cuales, el sistema autograbante ha ganado terreno por ser una técnica más sencilla. El objetivo del estudio fue evaluar comparativamente el valor de resistencia al push-out medido en megapascales (Mpa) de postes de fibra de vidrio cementados con un cemento de resina utilizando un adhesivo universal con modalidad grabado convencional y modalidad de autograbado. Material y método: En 10 dientes unirradiculares se realizaron tratamientos endodónticos y fueron divididos aleatoriamente en 2 grupos en donde con cemento de resina Relyx Ultimate y adhesivo universal Single Bond Universal (SBU) se cemento un poste de fibra. Grupo RCA: Aplicación de SBU modalidad grabado convencional. Grupo RS: Aplicación de SBU modalidad autograbado. Luego de 48 horas los dientes fueron seccionados en el tercio cervical, medio y apical dando un total de 30 muestras (n=30). La prueba de push-out fue realizada con la maquina Tinius Olsen H5K-S. Las muestras fueron observadas bajo microscopia óptica con un aumento de 4X para determinar el modo de falla. Resultados: Los valores fueron expresados en Mpa y analizados estadísticamente, por el software SPSS 15.0 utilizando el test de Shapiro-Wilk y T-Student con un nivel de significancia del 95%. Resultados: Los valores mostraron que no existe diferencia estadísticamente significativa entre los dos grupos estudiados (p>0,05) obteniéndose un promedio y una desviación estándar (±DS) para el grupo RCA fue de 12.33 (±3.17) y el grupo RS 12.02 (±2.45). Conclusión: No se encontró diferencia estadísticamente significativa en los valores de resistencia al push-out en los postes de fibra con adhesivo SBU modalidad autograbado y modalidad grabado convencional. Palabras claves: Poste fibra, Adhesivo Universal, Cemento de resina SUMMARY The most common failure in the rehabilitation of endodontically treated piece by fiber post and coronary reconstruction is the debonding of the post, probably due to poor adhesion between post, cementing medium and tooth. Currently intradicular cementation and bonding is one of the most investigated and most controversial because of multiple systems on the market, like self-etching system, has gained ground with little evidence regarding their clinical behavior. The push-out test is one of the in vitro test which evaluates clinical aspect as adhesive strength, therefore the purpose of this study was to compare in vitro "Significant difference, given by higher resistance value the push-out between fiberglass post cemented with RelyX® Ultimate (3M ESPE, Minnesota, USA) – Single Bond universal®(3M ESPE, Minnesota, USA) plus conventional etching (RSC) and fiberglass post cemented with RelyX® Ultimate(3M ESPE, Minnesota, USA) -Single Bond universal®(3M ESPE, Minnesota, USA) (RSA)”. 10 Single-rooted pieces were collected, which were divided into 2 groups: RSC Group: fiber post cemented with adhesive Single Bond Universal ® (3M ESPE, Minnesota, USA) with conventional Etching and RelyX Ultimate ® (3M ESPE, Minnesota, USA); RSA Group: fiber post cemented with RelyX Ultimate® (3M ESPE, Minnesota, USA) applying Single Bond Universal ® (3M ESPE, Minnesota, USA). After 48 hours, the teeth were sectioned at the third cervical and medium giving a total of 30 samples. Test was performed "push-out" in the Tinius Olsen H5K-S machine. The results were expressed in megapascals (MPa), the results were analised with Shapiro-Wilck test showing a normal distribution (p>0.05). The corresponding descriptive analysis, where it was found an average and standard deviation (± SD) for RCA of 12.33 (± 3.17) and 12.02 RS (± 2.45). Using t-student test which resulted in that no significant difference between each of the groups (p <0.05). Conclusion: There is no significant difference in the resistance value between RCA and RS. Keywords: Fiber Post, self-etching adhesive, resin cementes
dc.language.isoeses
dc.publisherUniversidad Andrés Belloes
dc.relation.ispartofseries617.6 R288cd 2014;
dc.subjectOdontología; Poste fibra; Adhesivo Universal; Cemento de resinaes
dc.titleResistencia adhesiva en postes de fibra utilizando adhesivo universal con diferentes sistemas de grabadoes