Show simple item record

dc.contributor.authorParedes-García, Verónica
dc.contributor.authorToledo, Néstor
dc.contributor.authorJuliano, Denardin
dc.contributor.authorVenegas-Yazigi, Diego
dc.contributor.authorCruz, Carlos
dc.date.accessioned2014-02-24T17:04:02Z
dc.date.accessioned2016-05-24T20:29:32Z
dc.date.available2014-02-24T17:04:02Z
dc.date.available2016-05-24T20:29:32Z
dc.date.issued2013
dc.identifier.citationJournal of the Chilean Chemical Society. Vol. 58. N° 4, 2013.es
dc.identifier.issn0717-9707
dc.identifier.urihttp://repositorio.unab.cl/xmlui/handle/ria/2360
dc.descriptionIndexación: Scieloes
dc.description.abstractABSTRACT In this work we present the synthesis and characterization of iron oxide nanoparticles (IONPs), which were structurally and magnetically characterized. The use of iron salts and an organic acid (l-serine or ascorbic acid) as precursors under solvothermal conditions yielded these coated IONPs. The powder X-ray diffraction pattern of FeO-1 and FeO-2 is consistent with hematite (α-Fe2O3) and hematite-maghemite ((α-Fe2O3/γ-Fe2O3) respectively. The TEM analysis permits to estimate an average size of 10 nm for the FeO-1 sample. The magnetic characterization of the samples through the M(H) plots showed a very low coercivity value for both samples, being 53 Oe for FeO-1 and 10 Oe for FeO-2, indicating the very weak ferromagnetic character of the synthesized iron oxide species. Even though both organic acids under solvothermal conditions permit to obtain coated IONPs in one pot reaction, l-serine produces a more narrow-size distribution.es
dc.language.isoenes
dc.publisher2014 Sociedad Chilena de Químicaes
dc.subjectIron oxide, nanoparticles, hematite, maghemite, solvothermal synthesis, magnetismes
dc.titleOne pot solvothermal synthesis of organic acid coated magnetic iron oxide nanoparticleses