dc.descriptionTesis (Cirujano Dentista)es_CL
dc.description.abstractIntroducción: El uso de sistema espiga muñón colada para rehabilitación en base a prótesis fija unitaria sigue siendo muy utilizada hoy en día. Sin embargo, estas presentan una alta tasa de fracasos, manifestadas sobre todo por su desalojo, siendo un factor importante, el poco tiempo de espera que se deja para realizar el tallado definitivo del muñón luego de la cementación de la espiga. La preparación biológica genera ciertas vibraciones en el diente, que pueden afectar la capa de cemento entre este y el perno, disminuyendo sus propiedades de resistencia ante la tracción. El objetivo de este estudio es evaluar la influencia del tiempo transcurrido antes del tallado de la preparación biológica, luego de cementar las espigas muñones coladas con cemento de vidrio ionómero y cemento fosfato de zinc, en la resistencia traccional de estas. Materiales y métodos: se utilizaron 40 premolares inferiores unirradiculares recién extraídos, a los cuales se les realizó un tratamiento de endodoncia convencional. Luego se les realizó un corte a nivel del límite amelocementario proximal, se desobturaron a una longitud de 10 mm, fueron montados sobre un bloque de acrílico y enviadas al laboratorio para la confección de las espigas coladas. La muestra fue divida al azar en 4 grupos de 10 dientes cada uno: en los grupos 1 y 3 las espigas coladas fueron cementadas con cemento vidrio Ionómero y en los grupos 2 y 4 con cementos fosfato de zinc. A su vez, las muestras fueron divididas en el tiempo de espera para tallar, donde el grupo 1 y 2 fueron tallados después de una semana de haber cementado la espiga muñón, mientras que los grupos 3 y 4, a los 10 minutos después de haber cementado la espiga muñón. Posteriormente las muestras fueron sometidas a pruebas de tracción en una máquina de tracción, a una velocidad de 5mm/min. Los datos fueron expresados en Megapascales (Mpa), los que se analizaron estadísticamente por medio del test Shapiro-Wilk, One-WayAnova y Tukey. Resultados: el promedios más alto lo presentó el grupo 1(cemento vidrio ionómero/1 semana) (3,115 Mpa) y fue significativamente mayor que los obtenidos por los grupos 2(cemento fosfato de zinc/1 semana) (2,6140 Mpa), 3 (cemento vidrio ionómero/10 minutos) (2,3170 Mpa) y 4 (cemento fosfato de zinc/10 minutos) (1,7440 Mpa). El grupo 1 fue superior al grupo 3 y el grupo 2 fue superior al grupo 4. Además no hubo una diferencia significativa en el promedio entre el grupo 1 y 3 (2,716 Mpa), y el grupo 2 y 4 (2,179 Mpa). Conclusión: El tiempo transcurrido entre la cementación de la espiga muñón colada y el tallado de la preparación biológica es un factor que influye significativamente en la resistencia a la tracción de las espigas. No existen diferencias estadísticamente significativas de los valores de resistencia a la tracción entre los cementos estudiados.es_CL
dc.description.abstractTitle: Influence of waiting time in core finishing, in the tensile strength of cast post cemented with glass ionomer and Zinc Phosphate. Introduction: The use of cast post in the rehabilitation based on crowns is still widely used today. However, these have a high failure rate, shown mainly by the displacement, being an important factor, the short waiting time that is left for the final core finishing of the cast post after the cementing of the cast post. The biological preparation generates some vibrations in the tooth, which can affect the cement layer between it and the cast post, reducing its resistance to traction. The objective of this study is to evaluate the influence of the time elapsed before core finishing the biological preparation, after cementing the cast post with glass ionomer cement and phosphate cement, in the tensile strength of these. Materials and methods: 40 freshly extracted single-rooted lower premolars were used, which underwent conventional endodontic treatment. Later, a cut at the proximal cement enamel junction was made, they were desobturation to a length of 10mm, were mounted on an acrylic block and sent to the laboratory for the preparation of the cast post. The sample was randomly divided into 4 groups of ten teeth each: groups 1 and 3 the cast post were cemented with glass ionomer cement and in groups 2 and 4 with zinc phosphate cement. In turn, the samples were divided by waiting time, were groups 1 and 2 were cut after a week of having cemented the cast post, while groups 3 and 4, 10 minutes after cementing the cast post. The samples were later subjected to tensile testing in a tensile testing machine at a speed of 5mm / min. Data was expressed in megapascals (MPa) and was statistically analyzed using the Shapiro-Wilk, One-WayAnove and Tukey test. Results: The highest average was presented by group 1 (glass ionomer cement / 1 week) (3,115 Mpa) and was significantly higher than those obtained by group 2 (zinc phosphate cement / 1 week) (2,6140 MPa), 3 (glass ionomer cement / 10 minutes) (2,3170 MPa) and 4 (zinc phosphate cement / 10 minutes) (1,7440 MPa). Group 1 was higher than group 3 and Group 2 was higher than group 4. In addition there was no significant difference in the average between groups 1 and 3 (2,716 MPa) and groups 2 and 4 (2,179 MPa). Conclusion: the time between cementing of the cast post and the carving of the biological preparation is a factor the significantly influences the tensile strength of the cast post. No statistically significant differences in the values of tensile strength between the cements studied.
dc.language.isoeses_CL
dc.publisherUniversidad Andrés Belloes_CL
dc.subjectOdontologíaes_CL
dc.subjectMateriales dentaleses_CL
dc.subjectResistencia a la tracciónes_CL
dc.subjectCemento vidrio ionómeroes_CL
dc.subjectCemento fosfato de zinces_CL
dc.subjectChilees_CL
dc.subjectRegión metropolitanaes_CL
dc.subjectComuna de Macules_CL
dc.titleInfluencia del tiempo de espera para el tallado, en la resistencia traccional de espigas muñones coladas cementadas con vidrio ionómero y fostato de zinces_CL
dc.typeThesises_CL