Resistencia microtraccional de capa de adhesivo contaminada con sangre

Vista sencilla de ítem
dc.contributor.authorDe Nordenflycht, D
dc.contributor.authorKaplan, M
dc.contributor.authorMontecinos, V
dc.contributor.authorBáez, A
dc.date.accessioned2016-06-17T15:40:22Z
dc.date.available2016-06-17T15:40:22Z
dc.date.issued2013
dc.descriptionIndexación: Web of Science; Scielo.es
dc.description.abstractObjetivo: Evaluar la influencia de la contaminación con sangre en una capa de adhesivo formada sobre esmalte humano y su posterior descontaminación con NaOCl (2.5%) y etanol (70°) en la resistencia microtraccional. Métodos: La superficie vestibular de 80 premolares humanos fue fresada para obtener superficies planas sobre las que se aplicó un adhesivo de grabado y lavado siguiendo las indicaciones del fabricante (Adper Single Bond 2, 3M ESPE). Los premolares fueron distribuidos aleatoriamente en cuatro grupos: Grupo 1 (control), Grupo 2 (contaminación con sangre), Grupo 3 (descontaminación con NaOCl 2.5%) y Grupo 4 (descontaminación con etanol 70°). Luego, sobre cada premolar se confeccionó una corona de resina compuesta (Filtek Z350, 3M ESPE) y fueron cortados para obtener cuerpos de prueba de 1mm2 de sección transversal, los cuales fueron termociclados (5500 ciclos, 5-55°C) y traccionados hasta su límite de ruptura (Micro Tensile Tester, Bisco). Los resultados fueron analizados estadísticamente (ANOVA, Scheffe, p<0.05). Resultados: La resistencia microtraccional del Grupo 1 (24.8 MPa) fue significativamente superior al resto de los grupos (p<0.05). Las diferencias entre los grupos 2, 3 y 4 no fueron estadísticamente significativas (p>0.05). Conclusión: La contaminación con sangre de la capa de adhesivo interfiere significativamente en la resistencia microtraccional. La descontaminación con NaOCl o etanol no logró una recuperación de la resistencia microtraccional.es
dc.description.abstractAim: To evaluate the influence of blood contamination of the adhesive layer and posterior decontamination with NaOCl (2.5%) and ethanol (70º) on microtensile bond strength on human enamel. Methods: Vestibular surfaces of eighty human premolars were grounded to obtain flat surfaces. An etch-and-rinse adhesive was applied according to the manufacturer’s instructions (Adper Single bond 2, 3M ESPE). Teeth were randomly assigned into 4 groups: Group 1 (control), Group 2 (blood contamination), Group 3 (decontamination with NaOCl 2.5%) and Group 4 (decontamination with ethanol 70º). Then, a 4mm composite crown (Filtek Z350) was made and the teeth were vertically sectioned to obtain 1mm cross-section stick shape specimens. Specimens were thermocycled (5500 cycles, 5-55ºC) and pulled under tension until failure (Micro Tensile Tester, Bisco). Results were statistically analyzed (ANOVA, Scheffe’s test, p<0.05). Results: Microtensile bond strength in group 1 (24.8 MPa) was significantly higher than groups 2, 3 and 4 (p<0.05). The differences between groups 2, 3 and 4 were not significant (p>0.05). Conclusion: Blood contamination significantly interferes in microtensile bond strength. Decontaminating the blood residues with NaOCl or ethanol did not show a recovery of bond strength.en
dc.description.urihttp://ref.scielo.org/3zrh4b
dc.identifier.citationRev. Clin. Periodoncia Implantol. Rehabil. Oral vol.6 no.3 Santiago Dec. 2013es
dc.identifier.issn0719-0107
dc.identifier.otherhttp://dx.doi.org/10.4067/S0719-01072013000300003
dc.identifier.urihttp://repositorio.unab.cl/xmlui/handle/ria/806
dc.language.isoeses
dc.publisherSociedad de Periodoncia de Chile. Sociedad de Implantología Oral de Chile. Sociedad de Prótesis y Rehabilitación Oral de Chile.es
dc.subjectSangrees
dc.subjectContaminaciónes
dc.subjectResistencia adhesivaes
dc.subjectAdper Single Bond 2es
dc.subjectBloodes
dc.subjectBond strengthes
dc.titleResistencia microtraccional de capa de adhesivo contaminada con sangrees
dc.title.alternativeMicrotensile bond strength of adhesive layer contaminated with blood on human sound enameles
dc.typeArtículoes
Archivos
Bloque original
Mostrando 1 - 1 de 1
Miniatura
Nombre:
De Nordenflycht_resistencia_microtraccional.pdf
Tamaño:
690.55 KB
Formato:
Adobe Portable Document Format
Descripción:
TEXTO COMPLETO
Descargar
Bloque de licencias
Mostrando 1 - 1 de 1
No hay miniatura disponible
Nombre:
license.txt
Tamaño:
1.71 KB
Formato:
Item-specific license agreed upon to submission
Descripción:
Descargar
Colecciones
FO - Artículos de Revista