Efectos del té y los sistemas de pulido en la estabilidad del color de diferentes tipos de resina

Vista sencilla de ítem
dc.contributor.advisorVargas Bignotti, Pablo Enrique
dc.contributor.authorFerrari Buccioni, Nicole Natalia
dc.contributor.authorToledo Henríquez, Daniela Andrea
dc.contributor.editorFacultad de Odontología
dc.date.accessioned2017-04-13T18:38:35Z
dc.date.available2017-04-13T18:38:35Z
dc.date.issued2015
dc.descriptionTesis (Cirujano Dentista)es
dc.description.abstractObjetivo: Evaluar la estabilidad del color de resinas microhíbridas y de nanorelleno, sometidas a tinción con té y con distintos tratamientos de superficie. Materiales y métodos: 200 discos de resina clasificados en ocho grupos según tipo de resina (Nanorelleno o Microhíbrida), uso de glicerina para inhibir el oxígeno superficial y sistema de pulido (Sof-Lex o Enhance), luego fueron sumergidos en agua destilada por 24 horas a 37° C. Los discos se introdujeron en una solución de té, 10 minutos diarios, por dos semanas, seguidos de un cepillado diario. El color fue registrado previo a la exposición al té (T1), luego de siete días (T2) y a los catorce días (T3), a través de Espectrofotómetro Easyshade Vita, con escala de color Cie Lab. El análisis estadístico se realizó con sistema de varianza ANOVA y prueba LSD de Fisher, mediante el software Statgraphics Centurion XVII.I. Resultados: Se encontró diferencia significativa en la variación del color en los ochos grupos en los tiempos T1-T3 (p <0.05), existiendo diferencias significativas entre los 2 tipos de resina, presentando menor variación del color las resinas Filtek Z350 XT. Tanto para resina Filtek Z350 XT y Filtek Z250, el tratamiento de superficie que presentó menor susceptibilidad a la variación de color fue la inhibición de capa inhibida con Glicerina y sistema de pulido Sof-Lex. Conclusión: El grado de tinción de las resinas teñidas con té se ve afectado por el tipo de resina y por el tipo de tratamiento de superficie.es
dc.description.abstractObjective: To evaluate the color stability of microhybrid and nanofiller resins stained with tea under different surface treatments. Materials and methods: 200 discs resins were classified in eight groups according to: resin type (microhybrid or nanofiller), usage of glycerin, to inhibit surface oxygen and polishing method (Sof-Lex or Enhance). After this, they were immersed in distilled water for 24 hours at 37°C. The discs were immersed in a tea solution for a period of 10 minutes daily for two weeks, followed one brushing per day. The color was registered following: prior to exposure to tea (T1), after seven days (T2) and finally to fourteen days (T3), through Vita Easyshade spectrophotometer with Cie Lab color scale. The stadistic model used was an ANOVA and LSD Fisher, using the software Statgraphics Centurion XVII.I. Results: A significate difference was found among the eight groups in the times T1- T3 (P < 00.5), with significant differences between the 2 types of resins, having less color variation Filtek Z350 XT resins. Both Filtek Z250 and Filtek Z350 XT resins, the surface treatment showed less susceptibility to color variation was using glycerin and polishing Sof-Lex system. Conclusion: The type of resin and type surface treatment affects the grade of tea staining resins.
dc.identifier.urihttp://repositorio.unab.cl/xmlui/handle/ria/3327
dc.language.isoeses
dc.publisherUniversidad Andrés Belloes
dc.subjectResinas Compuestases
dc.subjectMateriales Dentaleses
dc.titleEfectos del té y los sistemas de pulido en la estabilidad del color de diferentes tipos de resinaes
dc.typeTesises
Archivos
Bloque original
Mostrando 1 - 1 de 1
No hay miniatura disponible
Nombre:
a115696_Ferrari_N_Efecto_del_te_y_los_2015_Tesis.pdf
Tamaño:
1.08 MB
Formato:
Adobe Portable Document Format
Descripción:
TEXTO COMPLETO ESPAÑOL
Descargar
Bloque de licencias
Mostrando 1 - 1 de 1
No hay miniatura disponible
Nombre:
license.txt
Tamaño:
1.71 KB
Formato:
Item-specific license agreed upon to submission
Descripción:
Descargar
Colecciones
FO - Trabajos de Titulación Pre-Grado